Aluminum Kitchen Cabinet Profile

Model: 6060 6061 6063 7005 7075

Aluminum profile

  1. Alloy: 6063, 6061
  2. Temper: T5/T6
  3. Colors: silvery white, bronze-colored, champagne, black, and others
  4. Surface treatment:

Anodizing

Electrophoresis

Powder coating

Wood grain

Mill finishing

  1. Thickness: above 0.7mm;
  2. Powder coated: Standard Germany RAL Mark;
  3. Al (min): 97%
  4. Alu ingot price: based on SMM.
  5. Sample time: two weeks after receiving the mold fee.

Primary Technical Data of Our Aluminum Profile

Chemical composition

Alloy Si Fe Cu Mn Mg Cr Zn Ti Impurity Al
6063 0.2-0.6 0.35 0.1 0.1 0.45-0.90 0.1 0.1 0.1 0.15 Rest
6061 0.4-0.8 0.70 0.15-0.40 0.15 0.8-1.2 0.04-0.35 0.25 0.15 0.15 Rest
6005 0.6-0.9 0.35 <0.1 <0.1 0.40-0.6 <0.1 <0.1 <0.1 <0.15 Rest

Mechanical property

Alloy Condition Tensile strength Yield strength Elongation Vickers hardness
6061 T6 >265Mpa >245Mpa >8%
6063 T5 >160Mpa >110Mpa >8% HV>58 HW>8
T6 >205Mpa >180Mpa >8%

Colored anodized profile

Grade Thickness of film Hole scaling quality of oxide layer
Average thickness Local thickness P. Cr acid-erosion weight less method
AA10 >10um >8mm <30 mg/d m2
AA15 >15um >12um

Electrophoretic coating profiles

Grade Anodic oxide film Thickness of paint film Thickness of complex film Film hardness
Average thickness Local thickness
A >10um >8um >12um >21um >3um
B >10um >8um >7um >17um >3um